Superconducting size effect in thin films under electric field: Mean-field self-consistent model
2019
We consider effects of an externally applied electrostatic field on superconductivity, self-consistently within a BCS mean field model, for a clean 3D metal thin film. The electrostatic change in superconducting condensation energy scales as $\mu^{-1}$ close to subband edges as a function of the Fermi energy $\mu$, and follows 3D scaling $\mu^{-2}$ away from them. We discuss nonlinearities beyond gate effect, and contrast results to recent experiments.
High-pressure characterization of multifunctional CrVO4
2020
[EN] The structural stability and physical properties of CrVO(4)under compression were studied by x-ray diffraction, Raman spectroscopy, optical absorption, resistivity measurements, andab initiocalculations up to 10 GPa. High-pressure x-ray diffraction and Raman measurements show that CrVO(4)undergoes a phase transition from the ambient pressure orthorhombic CrVO4-type structure (Cmcm space group, phase III) to the high-pressure monoclinic CrVO4-V phase, which is proposed to be isomorphic to the wolframite structure. Such a phase transition (CrVO4-type -> wolframite), driven by pressure, also was previously observed in indium vanadate. The crystal structure of both phases and the pressure …
MOCVD growth of CdO very thin films: Problems and ways of solution
2016
Abstract In this paper the growth of CdO by the MOCVD technique at atmospheric pressure has been studied in order to achieve very thin films of this material on r-sapphire substrates. The growth evolution of these films was discussed and the existence of a threshold thickness, below which island-shaped structures appear, was demonstrated. Some alternatives to reduce this threshold thickness have been proposed in the frame of the analysis of the crystal growth process. The morphology and structural properties of the films were analyzed by means of SEM and HRXRD. High-quality flat CdO samples were achieved with thicknesses up to 20 nm, which is five times thinner than the values previously re…
Structural characterization of TiO2/TiN O (δ-doping) heterostructures on (1 1 0)TiO2 substrates
2003
Abstract TiO2/TiNxOy δ-doping structures were grown on the top of (1 1 0)TiO2 rutile substrates by low pressure metal-organic vapor phase epitaxy (LP-MOVPE) technique at 750 °C. The samples were analyzed by high resolution transmission electron microscopy (HRTEM), electron energy loss spectroscopy (EELS) and X-ray diffraction techniques (rocking curves and φ-scans). The presence of satellites in the (1 1 0)TiO2 rocking curve revealed the epitaxial growth of 10 period δ-doping structures. The thickness of the TiO2 layers, 84 nm, was deduced from the satellites period. HRTEM observations showed around 1.5 nm thick δ-doping layers, where the presence of nitrogen was detected by EELS. The analy…
Oxidation resistance of Ti 3 AlC 2 and Ti 3 Al 0.8 Sn 0.2 C 2 MAX phases: A comparison
2019
Ti3AlC2 and Ti3Al0.8Sn0.2C2 MAX phase powders are densified using Spark Plasma Sintering technique to obtain dense bulk materials. Oxidation tests are then performed over the temperature range 800-1000°C under synthetic air on the two different materials in order to compare their oxidation resistance. It is demonstrated that, in the case of the Ti3Al0.8Sn0.2C2 solid solution, the oxide layers consist in TiO2, Al2O3 and SnO2. The presence of Sn atoms in
Rock-salt CdZnO as a transparent conductive oxide
2018
Transparent conducting oxides (TCOs) are widely used in applications from solar cells to light emitting diodes. Here, we show that the metal organic chemical vapor deposition (MOCVD)-grown, rock-salt CdZnO ternary, has excellent potential as a TCO. To assess this compound, we use a combination of infrared reflectance and ultraviolet-visible absorption spectroscopies, together with Hall effect, to determine its optical and electrical transport characteristics. It is found that the incorporation of Zn produces an increment of the electron concentration and mobility, yielding lower resistivities than those of CdO, with a minimum of 1.96 × 10 − 4 Ω · cm for a Zn content of 10%. Moreover, due to…
Optimization of physicochemical and optical properties of nanocrystalline TiO 2 deposited on porous silicon by metal-organic chemical vapor depositio…
2020
International audience; Titanium dioxide (TiO2) is very employed in solar cells due to its interesting physicochemical and optical properties allowing high device performances. Considering the extension of applications in nanotechnologies, nanocrystalline TiO2 is very promising for nanoscale components. In this work, nanocrystalline TiO2 thin films were successfully deposited on porous silicon (PSi) by metal organic chemical vapor deposition (MOCVD) technique at temperature of 550°C for different periods of times: 5, 10 and 15 min. The objective was to optimize the physicochemical and optical properties of the TiO2/PSi films dedicated for photovoltaic application. The structural, morphologi…
Induced crystallographic changes in Cd1−xZnxO films grown on r-sapphire by AP-MOCVD: the effects of the Zn content when x ≤ 0.5
2020
High-resolution X-ray diffraction, scanning electron microscopy and transmission electron microscopy techniques were used to investigate, as a function of the nominal Zn content in the range of 0–50%, the out-of-plane and in-plane crystallographic characteristics of Cd1−xZnxO films grown on r-plane sapphire substrates via atmospheric pressure metal–organic chemical vapor deposition. The study is conducted to search for knowledge relating to the structural details during the transition process from a rock-salt to a wurtzite structure as the Zn content increases in this CdO–ZnO system. It has been found that it is possible to obtain films exhibiting a single (001) cubic orientation with good …
Structural phase transition in [(C2H5)4N][(CH3)4N]ZnCl4
2019
The hybrid crystal [(C2H5)4N][(CH3)4N]ZnCl4 was studied using several experimental methods. DSC studies revealed the first order phase transition to the high temperature phase at about 496 K. This phase transition was confirmed in dielectric studies. Optical observation revealed the domain structure appearance characteristic for that of the phase transition between tetragonal and orthorhombic phases. This phase transition shows a lowering of symmetry as in the case of bromide analogs. Additionally, the optical studies showed the appearance of a number of cracks in the sample and in some cases, the samples became milky after cooling from the high temperature to the room temperature phase.
Structure and dielectric properties at phase transition of Na1/2Bi1/2TiO3-BaTiO3 solid solutions
2016
ABSTRACTPhase coexistence region is studied by x-ray diffraction for Na1/2Bi1/2TiO3-BaTiO3 solid solutions in the tetragonal phase side from the morphotropic phase boundary. The first order ferroelectric phase transition, determined from a jump in the temperature dependence of dielectric permittivity, is located inside the coexistence region of cubic and tetragonal phases and is below the temperature, where tetragonality disappears. At low BaTiO3 concentrations phase transition into ferroelectric state at cooling is slowly approached in time and is smeared over large temperature range. Rietveld method, applied for more precise evaluation of phase content, reveals large local deformations in…